Mullit Brick Description
Mullite bricks are sintered from mullite raw materials, and have good low thermal expansion, low creep, low thermal conductivity and good chemical stability. There are two types of mullite bricks. One is sintered mullite bricks, which are made by pressing natural mullite as the main raw material and adding additives. The other is re-sintered mullite brick, which is made by sintering synthetic mullite as the main raw material and additives.
Other popular refractory bricks
Technical Parameter
| Buyum | 75Mullite Brick | 70 Mullit g'isht | Mullite-corundum Brick |
| Al2O3 % | ≥75 | ≥70 | ≥80 |
| SiO2 % | ≤23 | ≤25 | ≤18 |
| Fe2o3 % | ≤0.4 | ≤0.4 | ≤0.3 |
| Bulk Density g/cm3 | ≥2.7 | ≥2.6 | ≥2.8 |
| Aniq g'ovaklilik % | ≤18 | ≤18 | ≤18 |
| Sovuq siqish kuchi MPA | ≥100 | ≥100 | ≥100 |
| (0.2Mpa,0.6%)Yukni yopishni yuklash ° C harorati boshlandi ° C | ≥1680 | ≥1680 | ≥1700 |
Vikipediyadan: Olov g'isht
Mullit g'isht zichligi
Umumiy engil mulit g'ishtining balandligi 0,6-1,2g / sm³, Og'ir mulitli qatli g'ishtlarning balandligi 2,3-2,5g / smɔ.
Mullite refirli g'ishtlari harorati nima?
Mullite qatlug'i g'ishtlarining harorati 1850 ga yaqin.
Mulite Refli g'ishtlar yuqori haroratlarda ishqorli qatliyotgan g'ishtlardan osonlikcha yo'q qilinadi. Bunga qo'chimcha, Yuqori haroratda, Mullit suv bug'ini alt2o3 hosil qilish va shikastlash uchun reaktsiyaga ta'sir qilishi mumkin. Shuning uchun, Mullitdan repressorli g'ishtlar yuqori gidroksidi va yuqori suv bug'lari kontentlari bilan uzoq vaqt davomida ishlatilmasligi kerak.
Mullite Referce g'ishtlarining ishlab chiqarish jarayoni
- Tarkibi: Kerakli Mullit Referga tegishli g'ishtlarning ishlashi bo'yicha talablariga muvofiq, turli xil xom ashyoni aniq torting, masalan, mullit, koni, va hokazo.
- Aralashtirmoq: Tortishtirilgan xom ashyoni mikserga qo'ying, Tegishli miqdordagi bog'lovchi va suv qo'shing, va xom ashyo taqsimlanishini yaxshilab aralashtiring.
- Qolip: Aralashtirilgan materiallar shakllantirish mashinasiga beriladi va ma'lum bir shakl va o'lchamdagi g'ishtga bosiladi.
- Quritish: Shakllangan g'isht quritish kamerasiga ovqatlanadi va keyinchalik o'q uzish uchun namlikni olib tashlash uchun qizdiriladi.
- Otash: Quritilgan g'ishtni otish uchun yuqori haroratli oshadi. Olovli harorat odatda 1500-1700 ℃, ingredientlarning tarkibiga qarab, Xom ashyolarning tozaligi va refirli g'ishtlarni bajarish uchun talablar.
- Sovutish va tekshirish: Ovozli mulitdan repitrli g'ishtlar tabiiy ravishda pishirilgan haroratga, so'ngra tashqi ko'rinish va ishlashni tekshirish va ishlash testi uchun ular sifatga mos kelishini ta'minlash uchun tashqi ko'rinishga ega bo'lishi kerak.
Mullit g'isht quyish narxi
Mullit g'isht va korund g'ishtini taqqoslash
| Mullit g'isht | Korund g'isht | |
| Xomashyo | Asosiy xom ashyo Mullitdir, odatda alyuminaning yuqori qismini o'z ichiga oladi (Al2O3) va silikon dioksid (SiO2). Mullit g'ishtlari Mullit sintezi bilan amalga oshirilishi mumkin, Yoki chang kabi yalpi va a-AL2O3 kukuni sifatida Mullit zarralarini ishlating. | Asosiy xom ashyo - bu Corbum rudasi. AL2O3 Crupunt g'isht miqdori odatda oralig'ida 72% va 90%. |
| Shlak qarshiligi | Mullit yuqori haroratlarda eritib, shlakning eroziyasiga qarshi turishi mumkin. | Uning asosiy tarkibiy qismi korund, ma'lum bir o'ziga xos sülositsion muhitda mulit g'ishtini ham ishlamasligi mumkin. |
| Termal zarba barqarorligi | Chapni isitish va sovutish muhitida yuqori kuch va barqarorlikni saqlab qolish. | Nisbatan kambag'al issiqlik zarbalari barqarorligi |
| Aşınmaya qarshilik | Kiyish qarshiligi yaxshi, lekin korundlik g'ishtidan biroz pastroq. | A'lo darajada torting |
| Yuqori haroratli ishlash | Yaxshi yuqori haroratli ishlash, yuqori erigan nuqta (Mull 1870 ℃) | Yuqori haroratning yuqori ishlashi yanada yuqori emas va erish nuqtasi yuqori (Corbum 2050 ℃) |
| Qo'llash sohalari | Blast pechlari, Temir eritish pechlari, Uglerod qora reaktorlari, shuningdek, shisha eritma pechlari va kulolchilik olovi. | Yuqori haroratli portlash pechlari, shuningdek, neft-kimyo sanoati kabi yuqori haroratli pechlar, Katta va o'rta o'lchamdagi sintetik ammiak gazifikasi pechlari va magnit materiallar pechlari. |