Preparation process of Nitride Bonded Silicon Carbide
Nitride Bonded Silicon Carbide uses high-purity silicon carbide powder, metal silicon powder and temporary binder. After batching, trộn lẫn, molding and drying, the silicon powder reacts with nitrogen to form silicon nitride crystal phase under high temperature and specific pressure conditions exceeding 1400 in a nitrogen atmosphere, and the silicon carbide particles are combined to form a high-temperature structural ceramic product.
Đồ nội thất lò khác
Nitride Bonded Silicon Carbide
Nitride Bonded Silicon Carbide（NBSIC） Parameter
| Item | Data | NBSIC Index |
| Mật độ số lượng lớn | g/cm3 | ≥2.65 |
| Porosity | % | ≤18 |
| Refractoriness under load | oC | ≥1700 |
| Cold bending strength | MPA | ≥40 |
| Si3N4 | % | ≥22 |
| SIC | % | ≥72 |
What are the advantages of silicon nitride combined with silicon carbide kiln furniture?
- Điện trở nhiệt độ cao: can maintain the same strength and hardness as normal temperature at high temperature of 1200-1400℃
- Cường độ cao: high flexural strength, especially at 1400℃, it still maintains the flexural strength index at room temperature
- Good thermal conductivity: thermal conductivity is 7~8 times that of general refractory materials
- Small thermal expansion coefficient: thermal expansion coefficient is half of high aluminum refractory materials
- Good oxidation resistance: can resist oxidation at high temperature and has a long service life
- Chống ăn mòn: acid and alkali corrosion resistance
Application field
Widely used in electrical porcelain, high aluminum and medium aluminum balls, grinding wheels, sanitary ware, and other special ceramic industries, oxide shelf brackets, vân vân.
Also used in the steel industry (for blast furnace waist lining masonry) and non-ferrous metallurgy industry (for electrolytic aluminum tank wall masonry)
Existing problems and correction directions
- Oxidation will occur during long-term use, affecting the service life of silicon nitride combined with silicon carbide kiln furniture
- Unreasonable support method is also an important reason for its damage
- Bending deformation is also an important problem of silicon nitride combined with silicon carbide kiln furniture during use
- Fragmentation will occur in an environment with temperature changes for a long time